transgranular stress corrosion cracking

基本解釋

• [冶金工程技術(shù)]穿晶應(yīng)力腐蝕開裂

英漢例句

雙語例句

• The results showed that it was chlorine ion that resulted in transgranular stress corrosion cracking in brass tubes.
  結(jié)果表明，黃銅琯的開裂爲(wèi)氯離子引起的穿晶應(yīng)力腐蝕開裂；
• The stress corrosion cracking sensitivity of the steel was low, and the fractography of its stress corrosion cracking showed transgranular and quasi-cleavage fracture with secondary cracks.
  研究表明該鋼具有較好的抗應(yīng)力腐蝕性能，其應(yīng)力腐蝕斷裂形貌爲(wèi)穿晶、解理斷裂，竝有二次裂紋。

• transgranular stress corrosion cracking更多例句

專業(yè)釋義

冶金工程技術(shù)

• 穿晶應(yīng)力腐蝕開裂