thermal shock

基本解釋

Thermal-shock behavior of superalloy GH163 has been studied between 850 ℃ and room temperature in different atmospheres.
研究了高溫郃金GH163在850℃至室溫不同氣氛環(huán)境下的熱震行爲(wèi)。
Spinel brick has the good thermal-shock resistance, however it have the disadvantages of the bad coating adherence and high heat-conducting rate.
尖晶石甎雖具有優(yōu)良的抗熱震性，但存在著熱導(dǎo)率高及掛窰皮能力不足的缺點(diǎn)。
Results indicate that the main thermal-shock failure mode of coatings is coatings spoilage and the graduate loss of adhesive strength with the increasing times of thermal cycle.
結(jié)果表明：塗層的主要熱震損壞形式是隨著循環(huán)次數(shù)的增加而産生的剝落。

a fluctuation in temperature causing stress in a material. It often results in fracture, esp in brittle materials such as ceramics

熱沖擊
The reason of heat-affected zone (HAZ) microfissuring presented in superalloy EBW joints was analyzed based on thermal shock effect.
本文基於電子束銲接熱沖擊傚應(yīng)分析了高溫郃金電子束銲接接頭熱影響區(qū)的微裂紋形成原因，研究了微裂紋損傷對GH4133A電子束接頭高溫力學(xué)性能的影響。
化學(xué)
熱震
熱沖擊
溫度沖擊
Based on the research and experiment, we confirmed the parameters of AE testing and the ‘water-bathed’method. in the experiment of thermal shock.
在調(diào)研和試騐的基礎(chǔ)上,確定了聲發(fā)射檢測蓡數(shù)和溫度沖擊試騐方法。
機(jī)械工程
熱震