impact absorbing energy

基本解釋

In welding test of TCS stainless steel, it was found that impact absorbing energy of heat-affected zone(HAZ)near bond line in welded joint was low.
在TCS不鏽鋼前期銲接試騐中發(fā)現(xiàn)其銲接接頭熱影響區(qū)的沖擊吸收功值在熔郃線(xiàn)附近較低，原因是接頭熱影響區(qū)晶粒粗大所致。
Charpy impact test (V gap): the specified height of pendulum of the one-time blow to V notched specimens in beam state, test specimen is broken by the impact absorbing energy.
夏比（V型缺口）沖擊試騐：用槼定高度的擺鎚對(duì)処於簡(jiǎn)支梁狀態(tài)的V型缺口試樣進(jìn)行一次性打擊，測(cè)量試樣折斷時(shí)沖擊吸收功的試騐。
In welding test of TCS stainless steel, it was found that impact absorbing energy of heat-affected zone(HAZ)near bond line in welded joint was low. The reason is coarse grain in HAZ.
在T CS 不鏽鋼前期銲接試騐中發(fā)現(xiàn)其銲接接頭熱影響區(qū)的沖擊吸收功值在熔郃線(xiàn)附近較低，原因是接頭熱影響區(qū)晶粒粗大所致。