vacuum evaporation

基本解釋

Connecting with the practice of vacuum evaporation decorative films, the role and technology of the paint spraying have been introduced.
結(jié)合真空蒸鍍裝飾膜的生產(chǎn)工藝，介紹了底涂料和面涂料的涂裝工藝及其作用。
Widely used in food, textile, pharmaceutical and chemical industries vacuum evaporation, condensation and impregnation, drying in the process.
廣泛用于食品、紡織、醫(yī)藥、化工等行業(yè)的真空蒸發(fā)、濃縮、浸漬、干燥等工藝過(guò)程中。
Ammonia and sulfuric acid (SO3) in and the reaction liquid after vacuum evaporation, concentration, crystallization, and then to liquid-solid separation processes obtained dry product.
氨水與硫酸（SO3）進(jìn)行中和反應(yīng)，反應(yīng)液經(jīng)過(guò)真空蒸發(fā)、濃縮、結(jié)晶，再進(jìn)行液固分離、干燥等工序制得產(chǎn)品。

真空蒸鍍
The silver quantum dots whose diameter is about 80nm were prepared successfully on the AAO template with the method of vacuum evaporation. Quantum dots whose diameter is the same as AAO template have uniform size, consistent and highly ordered nano-holes.
采用真空蒸鍍的方法,在AAO模板上成功的制備了銀量子點(diǎn),量子點(diǎn)的直徑與AAO模板納米孔的直徑相當(dāng),約80nm,大小均勻,排列與模板上納米孔的排列一致,高度有序。
真空涂膜
真空蒸發(fā)

真空蒸發(fā)
In this paper, several thin film samples of vanadium oxide were achieved with the method of vacuum evaporation and reaction R-F magnetron sputter, respectively high pure V2O5 powder as the source materials and metal vanadium as the target.
本論文以高純五氧化二釩和高純金屬釩分別作為蒸發(fā)源和濺射靶材，采用真空蒸發(fā)法和反應(yīng)射頻磁控濺射方法制備了氧化釩薄膜。
真空蒸鍍
真空蒸殼

真空蒸鍍
真空蒸發(fā)
Beyond 3 10-3 Pa vacuum degree ,three typical Ⅱ-Ⅵ selenium compound thin films, ZnSe, CdSe, (Zn, Cd) Se, have been obtained by vacuum evaporation technique on the substrate of glass.
在真空度達(dá)到3×10~(-3)pa以上時(shí)，用真空蒸發(fā)技術(shù)在玻璃襯底上獲得了ZnSe、CdSe、(Zn,Cd)Se三種類型的Ⅱ—Ⅵ族硒化物薄膜。
真空熱蒸鍍