as-cast condition

基本解釋

• 鑄造狀態(tài)

英漢例句

雙語(yǔ)例句

• The results show that austenite content is high and hardness is low as-cast condition.
  結(jié)果表明， 鑄鐵鑄態(tài)組織含奧氏體量多，硬度低；
• The ductile-embrittlement transition temperature of vermicular graphite cast iron increased with increasing phosphorus content both in the as-cast and annealed condition.
  蠕鐵的韌性——脆性轉(zhuǎn)變溫度鑄態(tài)和退火態(tài)均隨磷含量的增加而升高。
• The as-cast bainite steel studied in this paper could obtain bainite directly in the as-cast condition through alloying and controlling the cast cooling rate without heat treatment.
  所研究的鑄態(tài)貝氏體鋼是通過(guò)合金化和控制冷卻速度的方法在鑄態(tài)下直接得到貝氏體組織的，不需熱處理即可獲得所需的組織和性能。

• as-cast condition更多例句

詞組短語(yǔ)

短語(yǔ)

• as -ct condition -ct 鑄造狀態(tài)

• as-cast condition更多詞組

專業(yè)釋義

能源科學(xué)技術(shù)

• 鑄態(tài)

  Comparing the mechanical properties of Mg-4.2Zn-0.8Y alloy of T4 and T6 heat treatment with those of the as-cast condition, the tensile strength is improved by 17.2 and 37.7%, respectively, and the yield strength by 88.5 and 107.2%, respectively.2.
  結(jié)果顯示,熱處理能夠有效的提高合金的綜合力學(xué)性能, T4和T6處理態(tài)Mg-4.2Zn-0.8Y合金與鑄態(tài)相比,抗拉強(qiáng)度分別提高17.2%和37.7%;屈服強(qiáng)度分別提高88.5%和107.2%。

  機(jī)械工程

• 鑄態(tài)
• 鑄造狀態(tài)